Chemical composition(%)
C |
Mn |
Si |
S |
P |
Cu |
Cr |
Ni |
Mo |
Ti |
0.06-0.11 |
1.60-1.90 |
≤0.25 |
≤0.030 |
≤0.030 |
≤0.20 |
≤0.20 |
≤0.30 |
0.50-0.70 |
≤0.15 |
抗拉强度(MPa)
Rm(MPa) |
屈服强度(MPa)
Rp0.2(MPa) |
伸长率(%)
A(%) |
冲击功温度(-20℃)(J)
Akv(J) |
配合焊剂
Flux |
670 |
550 |
23 |
60 |
SJ101 |
C |
Mn |
Si |
S |
P |
Cu |
Cr |
Ni |
Mo |
≤0.10 |
0.40-0.70 |
0.15-0.35 |
≤0.030 |
≤0.030 |
≤0.20 |
0.80-1.10 |
≤0.30 |
0.40-0.60 |
抗拉强度(MPa)
Rm(MPa) |
屈服强度(MPa)
Rp0.2(MPa) |
伸长率(%)
A(%) |
冲击功温度(-20℃)(J)
Akv(J) |
配合焊剂
Flux |
590 |
500 |
26 |
72 |
SJ101 |
焊丝化学成份(范围)(%)
C |
Mn |
Si |
S |
P |
Cu |
Cr |
Ni |
Mo |
V |
≤0.10 |
0.40-0.70 |
0.15-0.35 |
≤0.030 |
≤0.030 |
≤0.20 |
1.0-1.3 |
≤0.30 |
0.50-0.70 |
0.15-0.35 |
抗拉强度(MPa)
Rm(MPa) |
屈服强度(MPa)
Rp0.2(MPa) |
伸长率(%)
A(%) |
冲击功温度(-20℃)(J)
Akv(J) |
配合焊剂
Flux |
640 |
550 |
24 |
112 |
SJ105 |
C |
Mn |
Si |
S |
P |
Ti |
Mo |
B |
其它 |
≤0.10 |
1.40-1.80 |
≤0.30 |
≤0.010 |
≤0.012 |
适量 |
适量 |
适量 |
(Cr+Ni+Cu)<0.5 |
抗拉强度(MPa)
Rm(MPa) |
屈服强度(MPa)
Rp0.2(MPa) |
伸长率(%)
A(%) |
冲击功温度(-20℃)(J)
Akv(J) |
配合焊剂
Flux |
610 |
500 |
28 |
160 |
SJ101 |
C |
Mn |
Si |
S |
P |
Ti |
Mo |
B |
其它 |
≤0.10 |
1.70-2.00 |
≤0.30 |
≤0.010 |
≤0.012 |
适量 |
适量 |
适量 |
(Cr+Ni+Cu)<0.5 |
抗拉强度(MPa)
Rm(MPa) |
屈服强度(MPa)
Rp0.2(MPa) |
伸长率(%)
A(%) |
冲击功温度(-20℃)(J)
Akv(J) |
配合焊剂
Flux |
675 |
575 |
28 |
140 |
SJ101 |
C |
Mn |
Si |
S |
P |
Ti |
Mo |
Ni |
B |
≤0.10 |
1.50-2.00 |
≤0.30 |
≤0.010 |
≤0.012 |
0.02-0.08 |
0.35-1.55 |
0.5-1.25 |
0.002-0.008 |
抗拉强度(MPa)
Rm(MPa) |
屈服强度(MPa)
Rp0.2(MPa) |
伸长率(%)
A(%) |
冲击功温度(-20℃)(J)
Akv(J) |
配合焊剂
Flux |
780 |
680 |
26 |
130 |
SJ101 |
C |
Mn |
Si |
Cr |
Ni |
0.04 |
1.82 |
0.34 |
20.13 |
9.50 |
抗拉强度(MPa)
Rm(MPa) |
伸长率(%)
A(%) |
607 |
41 |
焊丝化学成份(个例测量值)(%)
C |
Mn |
Si |
Cr |
Ni |
0.08 |
1.63 |
0.42 |
23.83 |
13.13 |
抗拉强度(MPa)
Rm(MPa) |
伸长率(%)
A(%) |
607 |
40 |